EFFECT OF NICKEL ELECTROPLATING TIME ON CORRUGATED METAL GASKETS PERFORMANCE

Article Sidebar

PDF
Published: Dec 1, 2021
DOI: https://doi.org/10.24853/sintek.15.2.123-129

Main Article Content

Isa Ibnu Ahbar
Universitas Negeri Yoggyakarta
Didik Nurhadiyanto
Universitas Negeri Yoggyakarta

Abstract

Metal gaskets is an alternative to asbestor gaskets, but it still have many weaknesses. The main focus of this research is to find the optimal electroplating time to prevent leakage.This research was started with forming the gasket material, and then followed by coating process. The methode that used in coating proses was electroplating with nickel solution. The gasket material used SUS 304 sheet with 1,5mm of thickness. Water pressure test was used to test leackage with 2 MPa, 4 MPa, 6 MPa, and 8 MPa presurre for 5 minute test duration. The result this research are  (1) electroplating are effected by time, the longer time applied more nickel attached to the gasket, (2) the best performance on nickel electroplated gasket was on 32 minute and 45 second plating time, (3) electroplated nickel gasket performance was better than the original to prevent leakage from 2 to 8 MPa water pressure.

Article Details

How to Cite
[1]
I. I. Ahbar and D. Nurhadiyanto, “EFFECT OF NICKEL ELECTROPLATING TIME ON CORRUGATED METAL GASKETS PERFORMANCE”, sintek. jurnal. ilm. teknik. mesin, vol. 15, no. 2, pp. 123–129, Dec. 2021.
Issue
Vol. 15 No. 2 (2021): SINTEK JURNAL
Section
Articles

Creative Commons License

  • Articles published in SINTEK JURNAL are licensed under a Creative Commons Attribution-ShareAlike 4.0 International license. You are free to copy, transform, or redistribute articles for any lawful purpose in any medium, provided you give appropriate credit to the original author(s) and SINTEK JURNAL, link to the license, indicate if changes were made, and redistribute any derivative work under the same license.
  • Copyright on articles is retained by the respective author(s), without restrictions. A non-exclusive license is granted to SINTEK JURNAL to publish the article and identify itself as its original publisher, along with the commercial right to include the article in a hardcopy issue for sale to libraries and individuals.
Author Biography

Isa Ibnu Ahbar, Universitas Negeri Yoggyakarta

Pendidikan Teknik Mesin

References

Peraturan Pemerintah Republik Indonesia No. 74 Tahun 2001 tentang Pengelolaan Bahan Berbahaya dan Beracun.

Pira, E., Donato, F., Discalzi G., Maida, L., .2017. Exposure to asbestos: past, present, and future diakses pada tanggal 30 Juni 2020 dari https://www.ncbi.nlm. nih.gov/pmc/articles/PMC5830559/

Saeed, H.A, Izumi, S., Sakai, S., Haruyama, S., Nagawa, M., Noda, H. 2008. Development of New Metallic Gasket and its Optimum Design for Leakage Performance, Journal of Solid Mechanics and Material Engineering 2: 1 pp. 105-114.

Haruyama, S., Nurhadiyanto, D., and Kaminishi, K. 2014. Contact Width Analysis of Corrugated Metal Gasket based on Surface Roughness, Advanced Material Research, Vol. 856 pp. 92-97.

Mazur, K, Stefanska, A. M. Herba, M. 2018. Analysis of chemical nickel plating process. Physicochemical Mechanics of Materials. No 3. pp. 89-95

Dibari, G.A., (2002) Nickel Plating. Diakses pada tanggal 30 Juni 2020 dari https://p2infohouse.org/ref/29/28180.pdf

Fadly, M.S., Iqbal, M., Magga, R.2019. Efek Variasi Arus Waktu Pencelupan Pada Proses Electroplating Plat Baja Komersil Terhadap Ketebalan Lapisan dan Laju Korosi. Jurnal Mekanikal, Vol. 10 No.1, pp. 906-917

Nurhadiyanto, D., Haruyama, S., Mujiyono,. Wahidin, A. (2020). Electroplating Process for Copper Coating of Corrugated Metal Gasket to Increase Performance, International Journaaof Mechanical Engineering and Technology, Vol. 11, Issue 1, pp.73-83.

Nurhadiyanto, D., Haruyama, S., Kaminishi, K., Karohika, IMG. Mujiyono, (2015), Contact Stress and Contact Width Analysis of Corrugated Metal Gasket, Applied Mechanics and Materials, Vol. 799-800 pp. 765-769.