Analisis briket fiber mesocarp kelapa sawit metode karbonisasi dengan perekat tepung tapioka

Istianto Budhi Rahardja, Cenda E Hasibuan, Yudi Dermawan

Abstract


This research aims to develop solid waste produced by oil palm plantation processing in the form of palm oil mesocarp fiber. Utilization which is usually only as boiler fuel in a Palm Oil Mill. Utilization of mesocarp fiber waste is to reduce waste, has a large heating value, and has a selling value. In the process of making mesocarp fiber briquettes, raw materials are provided, drying, charcoal (carbonization), filtering, forming 100 gr of charcoal with 150 ml, 200 ml, 300 ml of water solvent with tapioca starch adhesive (50 gr), and drying. The results of this research were briquettes with 150 ml solvent with a water content of 7.6%, an ash content of 22.52%, a burning time of 143 minutes, a burn rate of 0.21 %. The 200 ml solvent, namely: water content of 5.7%, ash content of 11.28%, burning time of 77 minutes, burning rate of 0.38 %. And in the 300 ml solvent, namely: water content of 5.2%, ash content of 16.84%, burning time of 67 minutes, burning rate of 0.36 %.


Keywords


briquettes; adhesives; fiber; carbonization

Full Text:

PDF

References


Istianto Budhi Rahardja, Wibowo Paryatmo, (2017). Analisa Dan Optimasi Sistem Pltgu Biomassa Gas Metan Dengan Daya 20 MW, Jurnal Teknologi, Universitas Muhammadiyah Jakarta, Vo.9, No.2, 2017,P. 65-76.

Mochammad Sahri, Fachrudin, Sabar Setiawidayat, (2019) Rancang Bangun Purwarupa Pembangkit Listrik Tenaga Biomassa, Proton, Vol. 11 No. 2 , 2019/Hal. 78-84

Cangara, M. Khairul Omaryadi (2020) Rancang Bangun Kompor Biomassa Portabel Penghasil Energi Listrik Berbasis Thermoelectric Generator. Skripsi-S1 Thesis, Universitas Hasanuddin.

Resti Ayu Widyarini, (2018). Analisis Sifat-Sifat Penyalaan Dan Pembakaran Briket Campuran Biomassa Sekam Padi Dan Bonggol Jagung, Skripsi, Universitas Padjajaran Bandung.

M Rifqi Aziz, Ahdiat Leksi Siregar, Azhar Basyir Rantawi, Istianto Budhi Rahardja, (2019). Pengaruh Jenis Perekat Pada Briket Cangkang Kelapa Sawit Terhadap Waktu Bakar, Prosiding Semnastek 2019, Universitas Muhammadiyah Jakarta. P. 1-9.

Renny Eka Putri, Andasuryani Andasuryani, (2017). Studi Mutu Briket Arang Dengan Bahan Baku Limbah Biomassa, Jurnal Teknologi Andalas, Vol. 21. No 2, (2017), P. 143-151.

Izzati, Kharisma, M. Mujiburohman, Kusmiyati, And , Eni Budiyati (2018) Pemanfaatan Limbah Padat Industri Serbuk Gergaji Kayu Menjadi Briket Sebagai Salah Satu Energi Alternatif. Skripsi Thesis, Universitas Muhammadiyah Surakarta.

Fardhan Arkan, (2017). Pemanfaatan Tempurung Kelapa Untuk Pembuatan Briket Arang Sebagai Potensi Energi Baru Pengganti Bahan Bakar Gas Di Desa Zed Kabupaten Bangka, Jurnal Pengabdian Kepada Masyarakat, Universitas Bangka Belitung, Vol 4, No.2 (2017), P. 1-9.

Arif Dedi Kurniawan, (2020). Pemanfaatan Limbah Serat (Fiber) Buah Kelapa Sawit Dan Plastik Daur Ulang (Polypropylene) Sebagai Material Komposit Papan Partikel (Particle Board), Vol.3, No.2 (2020)

Adi Ruswanto, (2019). Mengenal Teknologi Pengolahan Tandan Buah Sawit (TBS) Menjadi Minyak Kelapa Sawit, Instiper Yogyakarta.

Didi Dwi Anggoro, Muhammad Hanif Dzikri Wibawa, And Moch. Zaenal Fathoni,(2017). "Pembuatan Briket Arang Dari Campuran Tempurung Kelapa Dan Serbuk Gergaji Kayu Sengon," TEKNIK, Vol. 38, No. 2, Pp. 76-80, Dec. 2017.

Suhartoyo, Sriyanto Sriyanto, Effektifitas Briket Biomassa, Prosiding Snatif, 2017.

Standar Nasional Indonesia , (2000). Kualitas Briket, SNI 01-6235-2000.

Maliadin Lafose, (2019) Pengaruh Komposisi Perekat Terhadap Karakteristik Termal Briket Arang Kulit Biji Buah Jarak. Thesis, Universitas Halu Oleo.

Fajriatun Hasanah, (2020). Pembuatan Dan Karakterisasi Briket Campuran Kulit Durian (Durio Zibethinus Murr) Dan Tempurung Keluwak (Pangium Edule) Sebagai Bahan Bakar Alternatif, Unesa Journal Of Chemistry, Vol.9 No.2 (2020), P. 128-136.

Syafii, Andi Muhammad, (2020). Produksi Silika Xerogel Berbahan Baku Limbah Jerami Padi Berbantukan Metode Pirolisis Dan Metode Ekstraksi Sol-Gel, Disertasi Dan Thesis, Universitas Pertamina.

Budhi Indrawijaya, (2020). Pembuatan Briket Dari Kulit Buah Mahoni Dengan Variasi Jenis Dan Konsentrasi Perekat, Jurnal Ilmiah Teknik Kimia, Vol. 4 NO 2 (2020), P. 68-74.

Ricky Herjunata, Shafira Ratna Noviandini, Siti Diyar Kholisoh, (2020). Pengaruh Variasi Perekat Pada Briket Berbahan Limbah Tempurung Kelapa, Seminar Nasional Teknik Kimia Kejuangan. J11, 2020.

Guna Bangun Persada *A, Putty Yunesti, (2020). Pengaruh Temperatur, Komposisi Bahan Cangkang Inti Kelapa Sawit Dan Konsentrasi Perekat Pada Karakteristik

Briket Komersial Dari Tempurung Kelapa Sawit, PERSADA Et Al., Journal Of Science And Applicative Technology Vol. 4 (2), 2020, Pp. 126-132

Hendri Nurdin, Hasanudin, Darmawi, (2018). Karakteristik Nilai Kalor Briket Tebu Tibarau Sebagai Bahan Bakar Alternatif, INVOTEK: Jurnal Inovasi Vokasional Dan Teknologi, , Vol.18, No.1 (2018), P.19-24.

Yayah Yuliah, Sri Suryaningsih, Khoirima Ulfi, (2017). Penentuan Kadar Air Hilang Dan Volatile Matter Pada Bio-Briket Dari Campuran Arang Sekam Padi Dan Batok Kelapa, Jurnal Ilmu Dan Inovasi Fisika, Vol. 1, No 1 (2017), P. 51-57.

Siregar, Ade Erlinda, (2019). Proses Pembuatan Briket Bioarang Dari Pelepah Kelapa Sawit Dengan Variasi Waktu Karbonisasi Dan Rasio Perekat Sebagai Energi Baru Terbarukan, Skripsi, Fakultas Teknik, Universitas Sumatera Utara.

Ninis Hadi Haryanti, Rijali Noor, Dwi Aprilia, (2018). Karakterisasi Dan Uji Emisi Briket Campuran Cangkang Biji Karet Dan Abu Dasar Batubara, Prosiding Seminar Nasional Pendidikan

wan Hastiawan, (2018). Pembuatan Briket Dari Limbah Bambu Dengan Memakai Adhesive Pet Plastik Di Desa Cilayung, Jatinangor, Jurnal Aplikasi Iptek Untuk Masyarakat, Univesitas Padjajaran, Vol 7, No.3(2018), P. 154-156.

Azhar Basyir Rantawi, (2019). Mengetahui Kualitas Briket Cangkang Kelapa Sawit Menggunakan Perekat Arpus Sebagai Energi Alternatif, Jurnal Citra Widya Edukasi, Vol 11, No 3 (2019), P. 217-222.

Sri Suryaningsih, Otong Nurhilal, Komala Affiyanti Affandi, (2018). Pengaruh Ukuran Butir Briket Campuran Sekam Padi Dengan Serbuk Kayu Jati Terhadap Emisi Karbon Monoksida (CO) Dan Laju Pembakaran, Jurnal Ilmu Dan Inovasi Fisika, Vol. 8. No 1, (2018), P. 15-21.




DOI: https://doi.org/10.24853/sintek.16.2.82-91

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 SINTEK JURNAL: Jurnal Ilmiah Teknik Mesin

Powered by Puskom-UMJ