EMPOWERING ABU CANGKANG KELAPA SAWIT TERHADAP KUALITAS BATA BETON RINGAN (LIGHT-WEIGHT CONCRETE)

Istianto Budhi Rahardja; Vianda Nia C. Surbakti; Ahdiat L Siregar

doi:10.24853/jurtek.14.1.119-126

EMPOWERING ABU CANGKANG KELAPA SAWIT TERHADAP KUALITAS BATA BETON RINGAN (LIGHT-WEIGHT CONCRETE)

Istianto Budhi Rahardja, Vianda Nia C. Surbakti, Ahdiat L Siregar

Abstract

This research aims to determine the effect of adding oil palm shell ash on the quality of the resulting lightweight concrete bricks. Based on SNI 03-2847-2002, lightweight concrete is concrete containing light aggregate and unit weight between 800-1900 kg / m³. Making lightweight concrete bricks requires other materials in the mixing process, including silica sand. Silica sand is a major structural component in building and construction products, has the chemical formula SiO2 (silicon dioxides) which can be obtained from mineral, vegetable, and synthetic silica. Palm ash has pozzolanic properties and contains silica elements ranging from 31.45%, so that this element can be mixed with cement and produce higher mortar strength. In this research, the composition of the shell ash used was 15%, 30% and 45%, with variations in the composition of other ingredients. The results of calculations and testing, the addition of palm shell ash gave the quality of lightweight concrete bricks at 30% composition, with compressive strength: 13.43 MPa, density: 1.112.3 kg / m³ and water absorption capacity: 28.7%.

Keywords

Lightweight Concrete Brick, Shell Ash, Silica

Full Text:

PDF

References

Aziz, M. Rifqi, Ahdiat Leksi Siregar, Azhar Basyir Rantawi, Istianto Budhi Rahardja, (2019). Pengaruh Jenis Perekat Pada Briket Cangkang Kelapa Sawit Terhadap Waktu Bakar, Prosiding Seminar Nasional Sains dan Teknologi, Fakultas Teknik Universitas Muhammadiyah Jakarta, p. 1-10.

Badan Standarisasi Nasional, (2002). “Metode Pengujian Kekuatan Tekan Mortar Semen Portland Untuk Pekerjaan Sipil”, SNI 03-6825-2002, Jakarta

Badan Standarisasi Nasional.(2015). Standar Nasional Indonesia (SNI)15-2049- 2015.

Mulyati dan Reza Asrillina, (2018). Pengaruh Penggunaan Styrofoam Sebagai Pengganti Pasir Dan Zat Additive Sikament Terhadap Kuat Tekan Bata Beton Ringan, Jurnal Momentum Teknik Geodasi, Institut Teknik Padang, Vol. 20 No. 2, 2018, 110-116.

Nugroho, Ari Setyo (2014) Tinjauan Kualitas Batako Dengan Pemakaian Bahan Tambah Limbah Gypsum. Skripsi Thesis, Universitas Muhammadiyah Surakarta.

Nur, Muhammad, (2020). Analisis Kinerja Screening Pada Pengolahan Tambang Pasir Silika PT. Mitra Prima Sulawesi, Jurnal Geomining, Vol.1 No.1, 2020, 1-9

Ola, Alexius Luther dan Doly Prima Silaban, (2018). Komposit Bata Beton Ringan Dari Fly Ash Dan Bottom Ash Limbah Batubara Pabrik Minyak Nabati, Jurnal Riset Teknologi Industri, Vol. 12 No 1, Juni 2018, 47-55.

Permadi, Gangsar dan Lava Himawan, (2017). Studi Pembuatan Beton Ringan Non Aac (Non Autoclaved Aerated Concrete) Dengan Bahan Tambah Hidrogen Peroksida, Mill Dan Flyash 1 Bagi 1, Tugas Akhir, D3 Teknik Sipil SV, Universitas Gadjah Mada.

Pusat Penelitian Kelapa Sawit, (2011). Indonesian Oil Palm Research Institute”, Jalan Brigjen Katamso, Medan.

Putra, Hardiyanto Eka, Dharma Sardjana, Eddy Samsurizal, (2017). Studi Eksperimen Pengaruh Waktu Penuangan Adukan Beton Readymix Ke Dalam Formwork Terhadap Mutu Beton Normal, JeLAST : Jurnal PWK, Laut, Sipil, Tambang, Vol.4, No.4 (2017).P. 1-8.

Simanjuntak, (2011). Pembuatan dan Karakterisasi Batako Ringan dengan Memanfaatkan Sabut Kelapa Sebagai Agregat Untuk Bahan Kedap Suara, Universitas Sumatera Utara. Medan.

SNI 03-2847-2002. (2002). Persyaratan Beton Struktural Untuk Bangunan Gedung. Jakarta: Badan Standarisasi Nasional.

SNI-03-0348, 1989,(2002) Bata Beton Pejal, Badan Standar Nasional, Jakarta.

Sujatmiko, Bambang, Safrin Zuraidah , Wisnu Abiarto Nugroho, Elando Rizsa Putra Atmajaya, (2018).Penggunaan Pasir Silika Sebagai Substitusi Agregat Halus Untuk Meningkatkan Performance Bata Ringan, Rekayasa Jurnal Teknik Sipil, Vol.3, No.2 (2018), 5-12

Taufik, Hendra, Alex Kurniawandy, Deri Arita, (2017). Tinjauan Kuat Tekan Bata Ringan Menggunakan Bahan Tambah Foaming Agent, Jurnal Saintis, Vol.17, No.1 (2017), 52-62.

Tedja, Michael, (2014). Perbandingan Metode Konstruksi Dinding Bata Merah Dengan Dinding Bata Ringan, Comtech: Computer, Mathematics And Engineering Applications, Vol. 5 No. 1, (2014), 272-279.

Ukhtiyani, Indah, Darwati Darwis, Iqbal, (2017). Purifikasi Dan Karakterisasi Silika (Sio2) Berbasis Pasir Kuarsa Dari Desa Pasir Putih Kecamatan Pamona Selatan Kabupaten Poso, Natural Science : Journal Of Science And Technology, Vol.6, No.3, (2017), 270-275.

Vricilia, Meylinda, Ahmad Ridwan, Agata Iwan Candra, (2020). Kuat Tekan Pelat Beton Menggunakan Pasir Wlingi Dan Wiremesh Diameter 4 Mm, Jurnal Manajemen Teknologi & Teknik Sipil, Vol. 3, No. 2 (2020), 219-233.

Widiyatmoko, Sulistyo, Heru Sukanto, Purwadi Joko Widodo, (2016). Pengaruh Penambahan Sekam Padi Terhadap Kuat Tekan Dan Penyerapan Air Bata Ringan Jenis Cellular Lightweight Concrete (Clc), Jurnal Teknik Mesin Indonesia, Vol. 11, No. 1, (2016), 31-35.

DOI: https://doi.org/10.24853/jurtek.14.1.119-126